Poly(phenylene oxide) plastic compositions containing bis-phenoxy flame retardants

ABSTRACT

WHEREIN Z is bromine, m and m&#39;&#39; are integers having a value of 14, i and i&#39;&#39; are integers having a value of 1 or 2, alkylene is a straight or branched chain alkylene group having from 1 to 6 carbon atoms and A is cyano, nitro, lower alkoxy, lower alkyl, fluorine, dialkylamino, phenyl, halo-phenyl, benzyl or halobenzyl.   Plastic compositions containing poly(phenylene oxide) and bisphenoxy compounds having the formula:

llit States Anderson 1 1 *Mar. 4, 1975 POLY(PHENYLENE OXIDE) PLASTIC COMPOSITIONS CONTAINING BIS-PHENOXY FLAME RETARDANTS [75] Inventor: Arnold L. Anderson, Alma, Mich.

[73] Assignee: Michigan Chemical Corporation, St.

Louis, Mich.

[21] Appl. No.: 330,791

Related U.S. Application Data [63] Continuation-in-part of Ser. No. 260,240, June 6,

1972, abandoned.

[52] U.S. Cl. i. ,0jfl5,9 ;R,260/4575 R, 2 6 0/45.95 G [51] Int. Cl C08g 51/60 {58] Field of Search... 260/459 R, 45.95 G, 61 BB,

260/332 R, DIG. 24, 2.5 A]; 106/15 FP [56] References Cited UNITED STATES PATENTS 3,385,819 5/1968 Gouinlock 260/4575 R 3,560,441 2/1971 Schwancy et a]. 260/457 R 3,658,634 4/1972 Yanagi et a1 161/403 3,717,609 2/1973 Kutner 260/4595 G Primary Examiner-M. J. Welsh Attorney, Agent, or FirmRobert M. Phipps; James J. Mullen; Robert S. Frieman [57] ABSTRACT Plastic compositions containing poly(phenylene oxide) and bis-phenoxy compounds; having the formula:

wherein Z is bromine, m and m are integers having a value of 1-4, 1' and i are integers having a value of l or- 2, alkylene is a straight or branched chain alkylene group having from 1 to 6 carbon atoms and A is cyano, nitro, lower alkoxy, lower allcyl, fluorine, dialkyl amino, phenyl, halo-phenyl, benzyl or halo-benzyl.

17 Claims, No Drawings POLY(PHENYLENE OXIDE) PLASTIC COMPOSITIONS CONTAINING BlS-Pll-IENOXY FLAME RETARDANTS This application is a continuation-in-part of copending application Ser. No. 260,240, filed June 6, 1972 and now abandoned. The entire specification of this case, Serial No. 260,240, is to be considered as incorporated herein by reference.

The prior art considered in conjunction with the preparation of this application is as follows: U.S. Pat. Nos. 2,130,990, 2,186,367, 2,329,033, 3,666,692, 3,686,320 and 3,658,634; German Pat. No. 1,139,636; German Pat. No. 2,054,522; Japanese Pat. No. (72) 14,500 as cited in Volume 77, Chemical Abstracts, column l53737k(1972); Chemical Abstracts, Volume 13, column 448 Chemical Abstracts, Volume 31, column 7045 and Journal of the Chemical Society, pages 2972 2976 (1963). All of these publications are to be considered as incorporated herein by reference.

The present invention relates to plastic compositions containing poly(phenylene oxide), (herein referred to as PPO), and certain bis-phenoxy compounds (hereinafter defined) as flame retardants for said plastic com positions,

PPO plastics and utility thereof are known in the art as exemplified by Encyclopedia of Polymer Science and Technology Vol. 10, pages 92-111,.lohn Wiley & Sons, Inc., New York, 1969, and which publication is in toto incorporated herein by reference.

The need for flame retarding PPO plastics has also been recognized in the art as exemplified by Encyclopedia of Polymer Science and Technology, ibid, pages 100 and 103.

The resultant disadvantages in the utilization of various prior art materials as flame retardants for PPO include, without limitation, factors such as thermal migration, heat instability, light instability, nonbiodegradable, toxicity, discoloration and the large amounts employed in order to be effective.

Thus, there is always a demand for a material which will function as a flame retardant in poly(phenylene oxides) and, concurrently will not, by incorporation therein, adversely effect the chemical and/or physical and/or mechanical properties of the resultant poly(- phenylene oxide) plastic composition.

The prior art problem of providing a flame retarded poly(phenylene oxide) composition having desired chemical, physical and mechanical properties has now been substantially solved by the present invention and the above-described disadvantages substantially overcome.

Accordingly, one of the main objects of the present invention is to provide poly(phenylene oxide) plastic compositions which are flame retarded.

Another object of the present invention is to provide a material for poly(phenylene oxide) plastic compositions which will not substantially adversely effect the chemical and/or physical and/or mechanical properties of said compositions.

A further object of the present invention is to provide a flame retardant which is economic and easy to incorporate into poly(phenylene oxide) plastics without being degraded or decomposed as a result of blending or processing operations.

It has been found that the foregoing objects can be obtained by the incorporation of a new class of bisphenoxy compounds in poly(phenylene oxide) to subsequently provide flame retarded! compositions which exhibit outstanding chemical, physical and mechanical properties.

The bis-phenoxy compounds used in the present invention compositions have the formula:

In Formula I above, Z is bromine; m and m are integers each independently having a value of 1-4; i and i are integers each independently having a value of 1 or 2; alkylene is a straight or branched chain alkylene group having from 1 to 6 carbon atoms (e.g. Ch C H,, C3H6, CqHg, C5Hw, C6H|2 and and A is from the group cyano (--CH), nitro (NO lower alkoxy (e.g, OCH OC H lower alkyl (e.g. CH C H C 11 C.,H,,), fluorine, dialkylamino, e.g. N(CH N(C H phenyl (-C H halophenyl, benzyl (-CH C,,H and halo-benzyl.

ln Formula I, ior i is 1 when m or m is 4, respectively.

It is to be understood that all of the compounds falling within the above Formula 1 and as heretofore defined are generically described herein as bis-phenoxy" compounds.

Illustrative (but without limitation) of some of the present invention bis-phenoxy compounds are shown below:

the exemplary definitions of A, Z i, i, m, m and alkylene are listed in Table 1.

Table 1 Compound No. Z m m A 1 i' Alkylene 1 Br 2 2 -CN 1 1 CH 2 Br 2 2 F 1 1 C H, 3 Br 2 2 -CN 1 1 C l-1 4 Br 2 2 -CN 1 1 C l-1., 5 Br 2 2 -N0 1 t 1 C 11, 6 Br 2 2 OCH, 1 1 C H, 7 Br 3 3 -OC1-1 1 1 C H, 8 Br 2 2 -CH 1 1 C 11. 9 Br 2 2 F 1 1 C H l0 Br 2 2 -N(CH l l C 11 1] Br 2 2 -C,,H l 1 C H 12 Br 2 2 -C,,H Br 1 1 C H 13 Br 2 2 -CH C,,H 1 1 C H 14 Br 2 2 -CH C,,H ,Br 1 1 C H, 15 Br 3 3 -C,,H Cl 1 1 C H, l6 Br 3 3 F l l C H 17 Br 2 2 -CN 2 2 C l-1, l8 Br 4 4 -CN 1 l C l-I l9 Br 3 3 -C,,h Br l l C H 20 Br 3 3 -NO 2 2 C H 21 Br 2 2 'CN 1 1 CH(CH )CH 22 Br 4 4 -1 1O 1 1 CH(CH;,)CH C1-1 23 Br 3 3 F 2 2 CH CH(CH )CH CH 24 Br -C.,H 1 1 CH: 25 Br 1 1 -OC.,H 1 1 C H,

In general, the bis-phenoxy compounds are prepared by reacting a halogenated phenol with a halogenatedalkane at elevated temperatures in the presence of a basic material such as alkali metal hydroxides, carbonates, bicarbonates, oxides and hydrides. The preferred alkali metals are potassium and sodium. Where one desires to increase, for example, ease of handling the reaction mass, solvents such as ketones (e.g. acetone, methyl ethyl ketone, and methyl iso-butyl ketone), alcohols (e.g. methanol, ethanol, iso-propyl alcohol, butyl alcohol and glycols), or aqueous solvents (e.g. water, a mixture of water and alcohol and a mixture of water and ketone) can be employed. The desired end product, i.e. the bis-phenoxy compound, can be recovered from the reaction mass via various methods such as distillation or crystallization. Where the end product requires recovery via crystallization, various aromatic solvents such as benzene, toluene, xylene, dichlorobenzene and the like can be used.

Specifically, the bis-phenoxy compounds are prepared according to the following reactions:

(III) In the above reaction, X is halogen, preferably chlorine and alkylene is the same as herein defined. Where m and m and i and i are different integers, then equivalent molar portions of the particular halogenated phenol are used with equivalent portions of dissimilar halogenated phenol.

The above reaction is conducted at temperatures ranging from the freezing point of the initial reaction mass to the boiling point thereof. Preferably the temperatures are from about 40 C to about 200 C and more preferably from about 50 C to about 175 C. It is to be understood that the reaction can be conducted under sub-atmospheric (e.g. l/lO-8/l0 atmospheres), atmospheric or super-atmospheric (e.g. l.5lO atmospheres) pressure. Preferably, the reaction is carried out at atmospheric pressure.

The above-described processes can be carried out with conventional, readily available chemical processing equipment. For example, a conventional glass-lined vessel provided with heat transfer means, a reflux condenser and a mechanical stirrer can be advantageously utilized in practicing any of the preferred embodiments of the invention described in the examples set forth herein.

The amount of bis-phenoxy compound employed in the present invention compositions is' any quantity which will effectively render the poly(phenylene oxide) containing composition flame retardant. In general, the amount used is from about 1% to 25% by weight, based on the total weight of the composition. Preferably, the amount employed is from about to about 20% by weight. It is to be understood that any amount can be used as long as it does not substantially adversely effect the chemical and/or physical and/or mechanical properties of the end polymer composition. The amount utilized, however, is such amount which achieves the objectives described herein.

It is to be understood that the term poly(phenylene oxide) as used herein means products of the oxidative polymerization of phenols to poly(oxy phenylenes) which are also known as poly(phenylene oxides) or poly(phenylene ethers). This term also includes blends with other thermoplastics and/or plasticizers, however, the poly(phenylene oxide) comprises in all cases at least 50% by weight of the blend.

Thus the poly(phenylene oxide) used in the present invention compositions is any poly(phenylene oxide) herein defined and which one so desires to flame retard. It is to be understood that the poly(phenylene oxide) used can be a virgin material, i.e. substantially free of additives such as stabilizers, plasticizers, dyes, pigments, fillers, and the like, or the poly(phenylene oxide) can have additives (such as those mentioned and described herein) already contained therein or added concurrently with or after the addition of the bisphenoxy compounds.

Another facet of the present invention relates to the use of certain metal compounds with the bis-phenoxy compounds to promote a cooperative effect therebetween and thus enhance the flame retardancy of the resultant plastic composition as compared to the flame retardancy of either one component used separately. These enhancing agents are from the group antimony, arsenic, bismuth, tin and zinc-containing compounds. Without limitation, examples of said enhancing agents include Sb O SbCl SbBr SbI SbOCl, AS203, AS205, ZnBO BaB O.,-H O, 2-ZnO-3B O -35- H 0 and stannous oxide hydrate. The preferred enhancing agent is antimony trioxide.

The amount of enhancing agent employed in the present invention compositions is any amount which when used with said bis-phenoxy compounds will promote a cooperative effect therebetween. In general, the amount employed is from about l% to about 15%, preferably from about 2% to about 10%, by weight, based on the total weight of plastic composition. Higher amounts can be used as long as the desired end result is achieved.

It is also within the scope of thepresent invention to employ other materials in the present invention compositions where one so desires to achieve a particular end result. Such materials include, without limitation, adhesion promotors; antioxidants; antistatic agents; antimicrobials; colorants; flame retardants such as those listed on pages 456-458, Modern Plastics Encyclopedia, ibid., (in addition to the new class of flame retardants described herein); heat stabilizers; light stabilizers; pigments; plasticizers; preservatives; ultraviolet stabilizers and fillers.

In this latter category, i.e. fillers, there can be mentioned without limitation, materials such as glass; carbon; cellulosic fillers (wood flour, cork and shell flour); calcium carbonate (chalk, limestone, and precipitated calcium carbonate); metal flakes; metallic oxides (aluminum, beryllium oxide and magnesia); metallic powders (aluminum, bronze, lead, stainless steel and zinc); polymers (comminuted polymers and elastomer-plastic blends); silica products (diatomaceous earth, novaculite, quartz, sand, tripoli, fumed colloidal silica, silica aerogel, wet process silica); silicates (asbestos, kaolimite, mica, nepheline syenite, talc, wollastonite, aluminum silicate and calcium silicate); and inorganic compounds such as barium ferrite, barium sulfate, molybdenum disulfide and silicon carbide.

The above mentioned materials, including fillers, are more fully described in Modern Plastics Encyclopedia, ibid., and which publication is incorporated herein (in toto) by reference.

The amount of the above described materials employed in the present invention compositions can be any quantity which will not substantially adversely effect the desired results derived from the present invention compositions. Thus, the amount used can be zero (0) percent, based on the total weight of the composition, up to that percent at which the composition can still be classified as a plastic. In general, such amount will be from about 0% to about 75% and specifically from about 1% to about 50%.

The bis-phenoxy compounds can be incorporated in to the poly(phenylene oxide) at any processing stage in order to prepare the present invention compositions. In general, this is undertaken prior to fabrication either by physical blending or during the process of forming poly(phenylene oxide) per se. Where one so desires, the bis-phenoxy compounds may be micronized into finely divided particles prior to incorporation into the poly(phenylene oxide).

EXAMPLE I A poly(phenylene oxide) (PPO) plastic material, (GE 534-801, a product of General Electric Company and containing substantially no fillers is utilized as the base resin in order to prepare 26 formulations (plastic compositions). With the exception of formulation No. 1, the particular bis-phenoxy compound (and the antimony trioxide enhancing agent where indicated) is incorporated into the plastic by adding both to a Brabender mixer (Plastic-Corder, Torque Rheometer, Model PLV-l50, C. W. Brabender Instruments Inc.,

The resultant mixture is heated to about 320 C; at this temperature, it is in a molten state. The percentages of weight of each component utilized in the re spective formulations are listed in Table 11. Each formulation is discharged from the mixer and upon cooling solidifies and is ground into chips. The chips are subjected to compression molding in a Wabash press by placing said chips between two platens, the bottom of which contains four equal size depressions 3 inches by 5 inches by one-eighth inch deep. The top platen is then placed over the bottom platen and heat transfer means supplied thereto in order to melt said chips and thus provide solid samples (after cooling) for testing.

Portions of the samples of each respective formulation (Nos. 1-26) prepared according to the above described procedure are then subjected to two different standard flammability tests, i.e. UL 94 and ASTM D 2863-70. The UL 94 is, in general, the application of a burner to a test specimen (strip) for a certain period of time and observation of combustion, burning, and extinguishment. This procedure is fully set forth in Underwriters Laboratories bulletin entitled UL 94, Standard for Safety, First Edition, September 1972 and which is incorporated herein by reference. ASTM No. D-2863-70 is a flammability test which correlates the flammability ofa plastic specimen to the available oxy' gen in its immediate environment; this correlation is stated as an Oxygen Index, 0.1., level predicated upon the percent oxygen in the gaseous medium which is required to just provide a steady state of continuous burning of the plastic specimen. This ASTM method is fully described in 1971 Annual Book of ASTM Standards Part 27, published by the American Society For Testing and Materials, 1916 Race Street, Philadelphia, Pa.; this publication is to be considered as incorporated (in toto) herein by reference.

The results of these flammability tests are shown in Table 11.

TABLE II FLAMMABILITY DATA FOR PPO PLASTIC COMPOSITIONS CONTAINING BIS-PHENOXY COMPOUNDS FORMfigATION BIS-PIgJINOXY COMIZ7OUND ENHANCING AGENT OXYGEN INDEX UL 94 1. 2. 1 3. l 4. 2 5. 2 6. 5 7. 5 8. 7 9. 7 l0. 8 ll, 8 l2. l0 13. 10 I4. 12 15. 12 16. l4 l7. l4 l8. l6 l9. 16 20. 18 21v 18 22. 21 23. 21 24. 22 25. 22 25, 23

0 0 25.0 SB 20 0 28.5 SE-l 20 10 37.5 SE-O 20 0 27.5 SE-2 20 10 26.0 SE-O 20 O 27.0 SE-2 20 10 35.0 SE-O 20 0 28.0 513-2 20 10 36,0 SE-O 20 0 27.5 SE-Z 20 10 33.5 315-0 20 0 28.0 -1 20 10 35.5 SIT-0 20 0 29.0 SIS-0 20 10 395 SE-() 20 0 2915 Sli-t) 20 10 39.0 SEO 20 0 28.0 SE] 20 10 39.5 SE-O 20 0 30.0 SE-0 20 10 40.5 515-0 20 0 28.5 SEl 2O 10 39.0 SE-0 20 O 29.5 SE-() 20 10 40.0 SE-0 20 10 390 515-0 South Hackensack, N.J.). The mixer is equipped with a pair of roller type blades positioned within a head provided with heat transfer means.

Referring to Table II, the bis-phenoxy compound number relates to the structural formulae heretofore set forth in Table I; a difference of 2% in the Oxygen Index values'is considered significant; and the UL 94 values are on a graduated scale wherein the highest degree to lowest degree of flame retardancy is respectively SE-O, SE-l, SE-2, SB and Burns.

The results shown in Table II demonstrate the unique effectiveness of these bis-phenoxy compounds as flame retardants for poly(phenylene oxide). Specifically, formulation No. l (the control) had a 0.1. of 25.5 and UL 94 value of SB. In the even numbered formulations, the use of the particular bis-phenoxy compound results in a significant increase in fire retardancy as measured by 0.1. Formulation No. I had a SB rating, UL 94; however, the individual U.L. rating of SEQ for most of these formulations is, in this case, more indicative of increased flame retardancy.

The use of an enhancing agent such as Sb O to promote a cooperative effect between such agent and the bis-phenoxy compound is fully demonstrated via the results obtained from testing the odd numbered formulations. The highest UL 94 ratings and significantly higher 0.1. values are obtained by the use of an enhancing agent.

EXAMPLE II EXAMPLE lll Portions of the solid samples of Formulation Nos. l-26 prepared according to the above described procedure of Example I are subjected to the following ASTM tests in order to ascertain other properties of the resultant plastic composition:

Tensile Strength (at break) Flexural Strength Flexural Modulus Notched Izod Impact Heat Distortion Temperature (HDT) ASTM Test No. D638-6IT;

: ASTM Test No. D790-63;

: ASTM Test No. D790-63;

: ASTM Test No. D256-56; and

; ASTM Test No. 0648-56.

Each of the aforementioned ASTM Tests are standard tests in the art and are utilized collectively in order to ascertain the efficacy of a polymeric system as an overall flame retarded composition for commercial application. All of these ASTM Tests are to be considered as incorporated herein by reference.

The results of these ASTM tests show that the physical properties of the present invention compositions are basically the same (except 0.1. and UL 94 values) as the plastic material without the flame retardant (i.e. formulation No. 1). Thus, there is no substantial adverse effect on the physical properties of the plastic material when the novel compounds are incorporated therein.

EXAMPLE IV The procedure of Examples I, II and III are repeated except that the enhancing agent used is zinc borate instead of Sb O Substantially the same results are ob- 6 EXAMPLE v Samples of each of Formulation Nos. 1 through 26 Table II, are subjected to temperature (thermal) stability tests via the use of thermal gravimetric analysis (TGA). This test employed the use of a Thermal Balance, model TGS-l, Perkin-Elmer Corporation, Norwalk, Conn., and an electrical balance, Cahn 2580 model, Cahn Instrument Company, Paramount, Calif.

The results of these tests show that the bis-phenoxy' compound containing Formulations had more than adequate stability for melt processing and subsequent heat aging (i.e. high temperature applications) and thus demonstrating that the particular bis-phenoxy compounds are quite compatible with the plastic material. The bis-phenoxy compound stability thus aids in providing sufficient flame retardancy at the plastic decomposition temperature. This test also demonstrates that these compounds do not exhibit migration.

In view of the foregoing Examples and remarks, it is seen that the plastic compositions, which incorporate these compounds, possess characteristics which have been unobtainable in the prior art. Thus, the use of these compounds in the above described plastic material as flame retardants therefor is quite unique since it is not possible to predict the effectiveness and functionality of any particular material in any polymer system until it is actively undergone incorporation therein and the resultant plastic composition tested according to various ASTM Standards. Furthermore, it is necessary, in order to have commercial utility, that the resultant flame retarded plastic composition possess characteristics such as being non-toxic. Use of these compounds in the plastic material has accomplished all of these objectives.

The above examples have been described in the foregoing speciflcation for the purpose of illustration and not limitation. Many other modifications and ramifications will naturally suggest themselves to those skilled in the art based on this disclosure. These are intended to be comprehended as within the scope of this invention.

What is claimed is:

l. A plastic composition containing poly(phenylene oxide) having incorporated therein an effective amount of a flame retardannt which is a bis-phenoxy compound having the formula:

wherein Z is bromine; m and m are integers having a value of l-4; i and i are integers having a value of l or 2; alkylene is a straight or branched chain alkylene group having from I to 6 carbon atoms; and A is selected from the group consisting of cyano, nitro, lower alkoxy, lower alkyl, fluorine, dialkylamino, phenyl, halo-phenyl, benzyl, or halobenzyl, with the proviso that when m or m is 4, i or i respectively is l. 2. The composition as set forth in claim 1 wherein i and i are both 1.

3. The composition as set forth in claim I wherein i and i are both 2.

4. The composition as set forth in claim 2 wherein A A is halo-phenyl. is cyano. 12. The composition as set forth in claim 2 wherein 5. The composition as set forth in claim 2 wherein A A i b i is nitro- 13. The composition as set forth in claim 2 wherein 6. The composition as set forth in claim 2 wherein A 5 A is halo benzyl is lower alkoxy.

7. The composition as set forth in claim 2 wherein A is lower alkyl.

8. The composition as set forth in claim 2 wherein A 14. The composition as set forth in claim ll wherein alkylene is CH 15. The composition as set forth in claim ll wherein alkylene is C l-l is fluorine. 1O

9. The composition as set forth in claim 2 wherein A composltlon as Set forth m clam 1 is dialkylamino. alkylfine 1S a al I I 10. The composition as set forth in claim 2 wherein The composltlon as s forth In Claim 1 Whereln A is phenyl. alkylene is C H 11. The composition as set forth in claim 2 wherein 

1. A PLASTIC COMPOSITION CONTAINING POLY(PHENYLENE OXIDE) HAVING INCORPORATED THEREIN AN EFFECTIVE AMOUNT OF A FLAME REDARDANT WHICH IS A BIS-PHENOXY COMPOUND HAVING THE FORMULA:
 2. The composition as set forth in claim 1 wherein i and i'' are both
 1. 3. The composition as set forth in claim 1 wherein i and i'' are both
 2. 4. The composition as set forth in claim 2 wherein A is cyano.
 5. The composition as set forth in claim 2 wherein A is nitro.
 6. The composition as set forth in claim 2 wherein A is lower alkoxy.
 7. The composition as set forth in claim 2 wherein A is lower alkyl.
 8. The composition as set forth in claim 2 wherein A is fluorine.
 9. The composition as set forth in claim 2 wherein A is dialkylamino.
 10. The composition as set forth in claim 2 wherein A is phenyl.
 11. The composition as set forth in claim 2 wherein A is halo-phenyl.
 12. The composition as set forth in claim 2 wherein A is benzyl.
 13. The composition as set forth in claim 2 wherein A is halo-benzyl.
 14. The composition as set forth in claim 1 wherein alkylene is CH2.
 15. The composition as set forth in claim 1 wherein alkylene is C2H4.
 16. The composition as set forth in claim 1 wherein alkylene is C3H6.
 17. The composition as set forth in claim 1 wherein alkylene is C4H8. 